Semiconductor device and it&#39;s manufacturing method

ABSTRACT

In a FET having a thin-film SOI layer, to prevent a parasitic resistance increase in source/drain regions. To realize an upheaved layer to be formed on the source/drain region without using a lithography process and without a fear of a short circuit. Element-isolation insulating films  7 , which are taller than a semiconductor layer  3 , are formed surrounding the island-shaped semiconductor layer (SOI layer)  3 , while gate electrodes  5   a   , 8   a  which are taller than the element-isolation insulating films  7  are formed on the semiconductor layer  3 . A polycrystalline silicon film  11  is deposited on the whole surface. Upheaved layers  11   a   , 11   b  which are shorter than the element-isolation insulating film  7  are formed on the source/drain regions  3   a   , 3   b  by chemical-mechanical polishing and etching back. Silicide layers  13   a  to  13   c  are formed on the gate electrode and on the upheaved layers. An interlayer insulating film  14  is formed, and a metal electrode  16  is formed.

TECHNICAL FIELD

The present invention relates to a semiconductor device and its manufacturing method, and in particular, to a MOSFET formed on a silicon-on-insulator (hereinafter abbreviated as SOI) substrate having an SOI layer, and its manufacturing method.

BACKGROUND ART

In a case of forming a MOSFET using an SOI substrate in which a single crystal semiconductor layer (silicon layer) is formed on a semiconductor supporting substrate via an insulating film (mainly an oxide film), the insulating film is formed under the source region and the drain region of the MOSFET, whereby it is possible to reduce the parasitic capacity comparing to a case where a MOSFET is formed using a typical bulk substrate. As such, manufacturing an LSI with a use of an SOI substrate is advantageous for a speedup of the element, so that this method has been widely adopted.

In general, MOSFETs using SOI substrates may be of a full depletion type in which an SOI layer below the gate is fully depleted to be operated, or a partial depletion type in which an SOI layer is not fully depleted but is operated with a neutral region remained. Although a FET of the partial depletion type has an advantage that it can be manufactured using a forming method according to a process using a bulk substrate, there remains a neutral region which is electrically separated from the substrate. Thereby, a so-called substrate floating effect arises, in which the potential of the neutral region changes corresponding to the operational conditions and the operational current fluctuates. This makes a circuit design difficult. On the other hand, in a FET of the full depletion type, the potential below the channel does not fluctuate since there is no neutral region. Therefore, it has such an advantage that a stable circuit operation can be achieved.

However, transistors of the full depletion type are subject to a characteristic deterioration caused by a punch through and a short channel effect, comparing to transistors of the partially depleted type. In order to counter this defect, the film thickness of the SOI layer must be thinner. Generally, in order to keep the fully depleted operation, it is known that the film thickness of the SOI layer must be a ¼ length of the gate length or less. Therefore, if the gate length is 0.1 micron, the film thickness of the SOI layer must be 25 nm or less. However, if the film thickness of the SOI layer becomes thinner, the film thickness of the source/drain regions of the transistor becomes thinner, so that the resistance between the source/drain regions increases. In particular, if a metal silicide layer is formed on the source/drain region, the whole film thickness of the silicon layer is silicified, which causes a problem that an aggregation of silicide and breaking of wire may easily occur, whereby the parasitic resistance increases. Through our researches, we recognized that this phenomenon occurs remarkably if the film thickness of the SOI layer is 30 nm or less. In order to prevent the parasitic resistance increase, it is effective to locally thicken the silicon layer of the source/drain region. To cope with this, a method to raise a silicon layer on the source/drain region by the selective epitaxial growth has been proposed (for example, Japanese Patent Application Laid-open No. 2000-223713). This conventional art will be explained below with reference to drawings.

FIGS. 12(a) through 12(d) are sectional views showing the manufacturing method of the aforementioned conventional example in the order of steps. There is provided an SOI substrate in which a semiconductor layer 3 is formed on a supporting substrate 1 made of silicon, via a buried insulating film 2 consisting of an oxide film. As shown in FIG. 12(a), the semiconductor layer 3 serving as an active region is isolated by element-isolation insulating films 7 c, then a gate insulating film 4 is formed on the semiconductor layer 3, and a mask insulating film 9 consisting of a polycrystalline silicon film and a silicon nitride film is deposited thereon, then by patterning these, a gate electrode 22 is formed. Thereafter, sidewall insulating films 10 are formed on the side surfaces of the gate electrode 22 having the mask insulating film 9.

Next, as shown in FIG. 12(b), single crystal silicon is raised to have, for example, a film thickness of 50 nm under the silicon growth CVD conditions including HCI, to thereby form upheaved layers 11 e, 11 f. Then, by implanting into the semiconductor layer 3, using the ion implanting method, impurity atoms of a conductive type opposite to that of the semiconductor layer serving as a channel region, source/drain regions 3 a, 3 b are formed.

Next, as shown in FIG. 12(c), after the mask insulation film 9 is removed, cobalt, for example, is deposited on the whole surface by spattering to have a film thickness of 30 nm to 100 nm, and a heat treatment is performed to thereby form cobalt silicide layers 13 a, 13 b and 13 c. Then, the extra cobalt silicide layer is etched away, whereby the cobalt silicide layers 13 a, 13 b and 13 c are selectively remained.

Then, as shown in FIG. 12(d), an interlayer insulating film 14 consisting of an oxide film or the like is deposited on the cobalt silicide layers 13 a, 13 b and 13 c by the CVD. Here, the surface of the interlayer insulating film 14 may be flattened by the chemical-mechanical polishing (CMP). Then, contact openings 15 a, 15 b are selectively formed in the interlayer insulating film 14. Then, metal such as Al is deposited by spattering, and is patterned by the photolithography to thereby form a metal electrode 16 contacting the cobalt silicide layers 13 a, 13 b and 13 c via the contact openings 15 a, 15 b.

In a method of forming the upheaved layers using the aforementioned selective epitaxial growth method, facets are generated at the growth edges of the upheaved layers, which causes the width of the growth edges narrower. As such, it is difficult to form upheaved layers with low resistance. Further, the selective epitaxial growth needs a special CVD device suitable for the method, which causes the manufacturing cost to increase.

Further, in a case that silicon is raised under the condition that the facets are not formed at the growth edges of the upheaved layers, selectivity is degraded, whereby a special lithography process is required to prevent a short circuit. As a method of forming the upheaved layers in which selective growth is not performed and the lithography process is not required, there is proposed a method in which element-isolation insulating films are so formed as to be taller than the semiconductor layer (SOI layer), and by using CVD, CMP and the like, a conductive material such as silicon is buried into a dented portion defined by the gate electrode and the element-isolation insulating films.

In this case, however, the surface height of the gate electrode and the surface height of the upheaved layer coincide with each other, which causes a problem that a short circuit tends to occur when a silicide layer is formed.

It is an object of the present invention to solve the aforementioned problems in the conventional art, which object includes, first, to enable upheaved layers with low resistance to be formed to thereby reduce the parasitic resistance in source/drain regions, and secondly, to enable upheaved layers which are less possible to cause a short circuit to be formed without using a lithography process.

DISCLOSURE OF THE INVENTION

In order to achieve the aforementioned object, a semiconductor device according to the present invention comprises: a semiconductor layer which is formed on an insulating film or on an insulating substrate while being surrounded by element-isolation insulating films, and includes a channel region and a source/drain region; a gate electrode which is formed on the channel region via a gate insulating film while being surrounded by sidewall insulating films; and an upheaved layer which is made of a conductive material and is formed on the source/drain region. The semiconductor device has such a structure that the surface height of the gate electrode formed to be surrounded by the sidewall insulating films is higher than the surface height of the element-isolation insulating films, and the surface height of the upheaved layer is equal to or lower than the surface height of the element-isolation insulating films.

The upheaved layer is preferablely made of a polycrystalline silicon film, or a polycrystalline silicon film and a metal silicide film formed thereon, or a polycrystalline silicon film and a metal film formed thereon, or a metal silicide film, or a metal film.

Further, a method of manufacturing the semiconductor device according to the present invention comprises the steps of:

-   -   (1) forming, on an insulating film or on an insulating         substrate, element-isolation insulating films which surround a         semiconductor layer serving as a channel region and a         source/drain region and have a film thickness thicker than that         of the semiconductor layer;     -   (2) forming, on the semiconductor layer via a gate insulating         film, a gate electrode, the surface height of which is higher         than the surface height of the element-isolation insulating         films; and     -   (3) selectively forming, on the semiconductor layer, conductive         upheaved layers, which are surrounded by the element-isolation         insulating films and the gate electrode, and the surface height         of which is lower than the surface height of the         element-isolation insulating films.

Further, the method of manufacturing the semiconductor device according to the present invention may have such a structure including the steps of:

-   -   (1) depositing a first gate forming material layer and a mask         material layer via a gate insulating film on a semiconductor         layer formed on an insulating film or on an insulating         substrate;     -   (2) patterning the mask material layer, the first gate forming         material layer and the semiconductor layer so as to be island         shaped, and filling element-isolation grooves formed with         element-isolation insulating films;     -   (3) patterning the mask material layer and the first gate         forming material layer to thereby form a first gate electrode;     -   (4) forming first sidewall insulating films on the side surfaces         of the element-isolation insulating films and on the side         surfaces of a laminated body formed of the mask material layer         and the first gate electrode;     -   (5) filling dented portions surrounded by the first sidewall         insulating films on the semiconductor layer with conductive         upheaved layers and sacrifice fillers; and     -   (6) after removing the mask material layer, depositing a second         gate forming material layer and patterning it to thereby form a         second gate electrode.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a sectional view showing a first embodiment of the present invention in the order of steps, FIG. 2 is a sectional view showing the first embodiment of the present invention in the order of steps, and

FIG. 3 is a plan view showing the first embodiment of the present invention.

FIG. 4 is a sectional view showing a second embodiment of the present invention.

FIG. 5 is a sectional view showing a third embodiment of the present invention in the order of steps,

FIG. 6 is a sectional view showing the third embodiment of the present invention in the order of steps, and

FIG. 7 is a plan view showing the third embodiment of the present invention.

FIG. 8 is a sectional view showing a forth embodiment of the present invention in the order of steps, and

FIG. 9 is a sectional view showing the forth embodiment of the present invention in the order of steps.

FIG. 10 is a sectional view showing a fifth embodiment of the present invention in the order of steps, and

FIG. 11 is a sectional view showing the fifth embodiment of the present invention in the order of steps.

FIG. 12 is a sectional view showing a conventional example in the order of steps.

BEST MODE FOR CARRYING OUT THE INVENTION

Next, modes of carrying out the present invention will be described in detail in line with embodiments with reference to the drawings.

First Embodiment

FIGS. 1(a) through 1(e) and FIGS. 2(a) through 2(d) are schematic sectional views showing a manufacturing method of a semiconductor device according to a first embodiment of the present invention in the order of steps. In FIGS. 1 and 2, the dimensions in the vertical direction (up and down direction of the Figs.) are shown to be enlarged.

As shown in FIG. 1(a), first there is provided an SOI substrate in which, on a supporting substrate 1 made of silicon or the like, a buried insulating film 2 consisting of an oxide film with a thickness of 100 nm is formed, then on the insulating film 2, a semiconductor layer 3 made of silicon or the like is formed to have a film thickness of 5 nm to 60 nm. As a substitute for such an SOI substrate, an SOI substrate formed by an SIMOX (Separated by Implanted Oxygen) method in which oxygen is ion-implanted into a silicon supporting substrate, or an SOI substrate formed by laminating, may be used. Further, an SOI substrate in which a semiconductor layer is provided on an insulating substrate, such as an SOS (Silicon on Sapphire), may also be used.

Next, a channel region is formed by implanting impurity atoms in the semiconductor layer 3 using, for example, the ion implanting. Here, the concentration of the impurity atoms is set to be an impurity concentration appropriate for forming the channel region.

Next, on the semiconductor layer 3, a gate insulating film 4 with about 10 nm film thickness is formed by, for example, a thermal oxidation, and then on the gate insulating film 4, polycrystalline silicon, for example, is deposited to have a film thickness of about 50 nm so as to form a first gate material layer 5, and further a silicon nitride film 6 is formed to have about 100 nm thickness on the first gate material layer 5.

Next, as shown in FIG. 1(b), the semiconductor layer 3 serving as an element region, the gate insulating film 4, the first gate material layer 5 and the silicon nitride film 6 are processed to be island shaped by anisotropic etching.

Then, an insulating film 7 such as an oxide film is deposited to have about 200 nm film thickness on the whole surface by a deposition method such as the CVD. Then, by chemical-mechanical polishing (CMP), the insulating film 7 and a portion of the silicon nitride film 6 serving as a stopper film for the CMP are polished and flattened, to thereby form element-isolation insulating films 7 surrounding the island-shaped semiconductor layer 3. Thereby, the element-isolation insulating films 7 can be formed to have a structure raised above the semiconductor layer 3.

Next, as shown in FIG. 1(c), the silicon nitride film 6 is selectively etched away using phosphoric acid or the like. Then, on the first gate material layer 5, a second gate material layer 8 consisting of a polycrystalline silicon film is deposited to have about 100 nm film thickness by the CVD.

Next, as shown in FIG. 1(d), after a mask insulating film 9 consisting of a silicon nitride film or the like is deposited to have about 20 nm film thickness on the whole surface, the mask insulating film 9, the second gate material layer 8 and the first gate material layer 5 are etched in the order using a resist or the like as a mask, whereby a first gate electrode 5 a and a second gate electrode 8 a are formed.

Thereafter, by depositing an oxide film using the CVD to have a film thickness of, for example, 150 nm and continuing anisotropic etching, sidewall insulating films 10 are formed on the sidewalls of the laminated structure consisting of the mask insulating film 9, the second gate electrode 8 a and the first gate electrode 5 a, and on the sidewalls of the element-isolation insulating films 7, respectively. After this step has been completed, the exposed gate insulating film 4 is removed by etching. Note that prior to the sidewall insulating films 10 being formed, a halo region may be formed by implanting into the semiconductor layer 3 impurity atoms of a conductive type same as that of the channel region, or a source/drain extension region may be formed by implanting into the semiconductor layer 3 impurity atoms of a conductive type opposite to that of the channel region.

Next, as shown in FIG. 2(a), a polycrystalline silicon film 11 is deposited by the CVD to have about 300 nm film thickness on the whole surface.

Then, as shown in FIG. 2(b), the polycrystalline silicon film 11 is flattened by chemical-mechanical polishing, and then etched away so as to be in a height position lower than the surface height position of the element-isolation insulating films. Thereby, upheaved layers 11 a and 11 b consisting of the polycrystalline silicon film 11 are formed in dented portions surrounded by the element-isolation insulating films 7 and the laminated structure including the gate electrodes 5 a and 8 a, as shown in the Fig.

As described above, it is processed in such a manner that the polycrystalline silicon film 11 is deposited in the dented portions, and the surface of the polycrystalline silicon film 11 is polished and flattened by the CMP, then the polycrystalline silicon film 11 is removed by etching so as to have the required film thickness, whereby the upheaved layers 11 a and 11 b are formed. Therefore, the film thickness of the upheaved layers 11 a, 11 b can be uniform utilizing the characteristics of the etching. Further, since the film thickness of the upheaved layers 111 a, 11 b can be uniform, facets 11 d, shown in FIG. 12(b) showing the conventional example, are not formed on the upheaved layers 11 a, 11 b, whereby the polycrystalline silicon film 11 is filled in the portions which have been the facets 11 d conventionally. This enables resistance between a metal electrode 16 in the contact openings, described later, and the region of the semiconductor layer 3 to be reduced. It is also possible to further suppress an increase in the resistance by setting the thickness of the upheaved region to 30 nm or more.

Next, impurity atoms of a conductive type opposite to that of the channel are implanted by ion implanting into the second gate electrode 8 a, the first gate electrode 5 a and the upheaved layers 11 a, 11 b, and by performing a heat treatment, for example, at 1000° C. for 10 seconds, a conductivity is given to the polycrystalline silicon film while source/drain regions 3 a, 3 b of the opposite conductive type are formed in the semiconductor layer 3.

Next, as shown in FIG. 2(c), after the mask insulating film 9 on the gate electrode 8 a is removed (the mask insulating film 9 may be removed prior to the ion implanting process), cobalt, for example, is deposited by spattering on the whole surface to have a film thickness of 30 nm to 100 nm, and a heat treatment is performed, whereby cobalt silicide layers 13 a, 13 b and 13 c are formed.

Then, the extra cobalt is etched away, whereby the cobalt silicide layers 13 a, 13 b and 13 c are selectively remained. Here, the top surfaces of the upheaved layers 11 a, 11 b and the top surface of the gate electrodes (5 a, 8 a) have a difference in their heights, and a dented portion is formed on the gate electrode 8 a where the mask insulating film 9 is removed. Thereby, a short circuit between the upheaved layers 11 a, 11 b and the gate electrodes (8 a, 5 a) is prevented.

Then, as shown in FIG. 2(d), an interlayer insulating film 14 consisting of an oxide layer or the like is deposited on the whole surface by the CVD, and the surface of the interlayer insulating film 14 is flattened by chemical-mechanical polishing, if necessary. Then, by selectively etching away the interlayer insulating film 14, contact openings 15 a, 15 b are formed (a contact opening 15 c on the silicide layer 13 c is not shown).

Then, a metal electrode 16, contacting the silicide layers 13 a, 13 b and 13 c via the contact openings, is formed by depositing a metal film and patterning by the photolithography.

FIG. 3 is a plan view showing the first embodiment of the present invention, and a sectional view taken along the line III-III in FIG. 3 is shown in FIG. 2(d).

As described above, the dented portions are formed by such a structure that the element-isolation insulating films 7 are raised above the semiconductor layer 3, and the sidewalls of the element-isolation insulating films 7 and the gate electrodes 5 a, 8 a are covered with the sidewall insulating films 10, respectively. Further, the upheaved layers 11 a, 11 b can be formed to be buried in a self-aligned manner on the source/drain regions 3 a, 3 b in the dented portions by the film deposition using the CDV and by flattening and etching using the CMP. Therefore, in the present invention, it is not required to use a selective epitaxial growth like the conventional method, nor specific processing. Further, facets, which cause a problem in the selective epitaxial growth method, will never be generated principally. Thus, this structure provides an advantage that the resistance can be reduced in a full scale. Further, since the element-isolation insulating films 7 are raised above the semiconductor layer 3, patterning by a photoresist or the like required in the structure where it is not raised is not necessary, whereby the steps can be simplified. Moreover, as shown in FIG. 3, the positions of the source/drain regions 3 a, 3 b and the upheaved layers 11 a, 11 b are not deviated and the margin between the adjacent regions can be shortened, so that there is an advantage of being miniaturized. Further, by making the surface height of the gate electrodes 5 a, 8 a higher than the surface height of the upheaved layers 11 a, 11 b, and by forming silicide in the dented portion surrounded by the sidewall insulating films 10 on the gate electrodes 5 a, 8 a, it is possible to effectively prevent a short circuit between the gate electrodes 5 a, 8 a and the source/drain regions 3 a, 3 b without expanding the area (without sacrificing the integration degree).

As described above, in the semiconductor device of the present invention, even in the case of using an SOI substrate in which the film thickness of the semiconductor layer 3 is 30 nm or less whereby the parasitic resistance of the source/drain regions 3 a, 3 b increases, the upheaved layers 11 a, 11 b can be formed to have any film thickness in a self-aligned manner, whereby it is possible to reduce the resistant value of the parasitic resistance in the source/drain regions 3 a, 3 b.

Second Embodiment

FIG. 4 is a sectional view showing a second embodiment of the present invention. In FIG. 4, the dimension in the vertical direction (up and down direction in the Fig.) is shown to be enlarged.

A semiconductor device according to the second embodiment shown in FIG. 4 includes, a buried insulating film 2 formed on a supporting substrate 1, a semiconductor layer 3 consisting of a silicon film, source/drain regions 3 a, 3 b formed in a portion thereof, element-isolation insulating films 7 surrounding the semiconductor layer 3, a gate insulating film 4 formed on the semiconductor layer 3, a first gate electrode 5 a and a second gate electrode 8 a, sidewall insulating films 10 formed on the sidewalls of the gate electrodes, upheaved layers 11 c, 11 d consisting of a metal silicide film formed to be buried in dented portions surrounded by the element-isolation insulating films 7 (and the sidewall insulating films 10 thereof) and by the gate electrodes (and the sidewall insulating films 10 thereof), an interlayer insulating film 14 which covers the whole surface, and a metal electrode 16 which is formed on the interlayer insulating film 14 so as to contact the upheaved layers 11 c, 11 d via contact openings provided in the interlayer insulating film 14.

Although the upheaved layers 11 a, 11 b in the first embodiment consist of a polycrystalline silicon film, the upheaved layers 11 a, 11 b in the second embodiment consist of a metal silicide films.

In the embodiment shown in FIG. 4, the upheaved layers 11 a, 11 b do not consist of a silicon layer but consist of a metal silicide layer, which enables to realize the upheaved layers 11 a, 11 b with lower resistance. The upheaved layers 11 a, 11 b may consist of a metal silicide layer such as cobalt silicide, tungsten silicide, molybdenum silicide, and titanium ciliside. Instead of these metal silicide layers, the upheaved layers 11 a, 11 b may consist of a metal film such as a tungsten film which is formed via a barrier film such as a tungsten film or a titanium nitride film. By forming the upheaved layers 11 a, 11 b using a metal film in this way, it is possible to further reduce the resistance of the upheaved layers.

The upheaved layers 11 a, 11 b consisting of a metal silicide or a metal film as described above, can be easily formed by depositing the metal silicide or the metal films in the dented portions and flattening them by the CMP, and etching.

In this way, in the present invention, the upheaved layers 11 a, 11 b can be formed without utilizing a lithography technique even if metal silicide films or metal films, which have less selectivity than silicon films and are difficult in selective growth, are used.

Further, the upheaved layers 11 a, 11 b may be formed by depositing an amorphous silicon film and making it into polycrystalline by a heat treatment. By performing a heat treatment to the amorphous film, it is possible to form a silicon layer with a large grain size. This enables the upheaved layers 11 to have lower resistance than those being formed by depositing a polycrystalline silicon film.

Third Embodiment

FIGS. 5(a) through 5(e) and FIGS. 6(a) through 6(d) are schematic sectional views showing the manufacturing method in the order of steps of a semiconductor device according to a third embodiment of the present invention. In FIGS. 5 and 6, the dimensions in the vertical direction (up and down direction in Figs.) are shown to be enlarged.

First, as shown in FIG. 5(a), there is provided an SOI substrate which is so formed that on a supporting substrate 1 consisting of silicon or the like, a buried insulating film 2 consisting of, for example, an oxide film having a film thickness of 100 nm and a semiconductor layer 3 having a film thickness of 5 nm to 60 nm consisting of silicon or the like are laminated.

Next, impurity atoms of a first conductive type are implanted into the semiconductor layer by, for example, the ion implanting so as to be in a concentration appropriate for forming a channel region. Then, on the semiconductor layer 3, a gate oxide layer with about 10 nm film thickness is formed by, for example, a thermal oxidation, and on the layer, a first gate material layer 5 consisting of polycrystalline silicon or the like is formed to have about 50 nm film thickness and further a silicon nitride film 6 is formed to have about 200 nm film thickness, respectively.

Next, as shown in FIG. 5(b), the silicon nitride film 6, the first gate material layer 5, the gate insulating film 4 and the semiconductor layer 3 are anisotropically etched to be island shaped. Then, an insulating film (7) such as an oxide film is deposited on the whole surface by a depositing method such as the CVD to have a film thickness of about 300 nm. Then, by chemical-mechanical polishing, the insulating film (7) and a portion of the silicon nitride film 6 serving as a stopper film for the chemical-mechanical polishing are polished and flattened to thereby form element-isolation insulating films 7 surrounding the semiconductor layer 3 in the element region. Thereby, the element-isolation insulating films 7 are configured to be raised above the semiconductor layer 3.

Next, as shown in FIG. 5(c), a resist film (not shown) serving as a mask is formed by a typical photolithography on the region for forming the gate electrode, and the silicon nitride film 6 and the first gate material layer 5 are anisotropically etched to thereby form a first gate electrode 5 a which includes the silicon nitride film 6 on the surface thereof.

Next, after the resist film is removed, the silicon oxide film is deposited by the CVD to have a film thickness of, for example, 150 nm, and then anisotropically etched, whereby sidewall insulating films 10 are formed on the sidewalls of the gate electrode 5 a and the silicon nitride film 6 and on the inner sidewalls of the element-isolation insulating films 7, respectively. During this process, a portion of the gate insulating film 4 is etched and a portion serving as a source/drain region of the semiconductor layer 3 is exposed. Note that before the sidewall insulating films 10 are formed, a halo region may be formed by implanting into the semiconductor layer 3 impurity atoms of a conductive type same as that of the channel region, or a source/drain extension region may be formed by implanting into the semiconductor layer 3 impurity atoms of a conductive type opposite to that of the channel region.

Next, as shown in FIG. 5(d), in dented portions defined by the sidewall insulating films 10 on the element-isolation insulating films 7 and by the sidewall insulating films 10 on the silicon nitride film 6 and the gate electrode 5 a, a polycrystalline silicon film (11) is deposited by the CVD to have a film thickness of about 300 nm, and is flattened by chemical-mechanical polishing, then the polycrystalline silicon film is etched to thereby form upheaved layers 11 a and 11 b consisting of the polycrystalline silicon film in the dented portions surrounded by the element-isolation insulating films 7 and the gate electrode 5 a as shown in the Fig.

In this way, since the element-isolation insulating films 7 are raised above the semiconductor layer 3 so as to form the dented structure, not only the element-isolation insulating films 7 raised serves as the stopper for the CMP in the process of performing the CMP to the polycrystalline silicon film, but also the film thickness of the upheaved layers 11 a, 11 b can be formed to be uniform due to the dented structure. Further, by setting the thickness of the upheaved layers 11 a, 11 b to be 30 nm or more, it is possible to suppress an increase in the resistance. The reason is the same as that described in the first embodiment.

Next, impurity atoms of a conductive type opposite to that of the channel are implanted into the upheaved layers 11 a, 11 b by ion implanting, and by performing a heat treatment at, for example, 1000° C. for 10 seconds, source/drain regions 3 a and 3 b are formed in the region of the semiconductor layer 3.

Next, as shown in FIG. 5(e), on the whole surface, an insulating film (18) consisting of, for example, an oxide film is deposited on the whole surface by the CVD and is processed by the CMP so as to be selectively remained on the upheaved layers 11 a, 11 b to thereby form a sacrifice insulating film 18.

Next, as shown in FIG. 6(a), the silicon nitride film 6 on the gate electrode 5 a is selectively etched away using phosphoric acid or the like, and a polycrystalline silicon film is deposited on the whole surface by the CVD and is given a conductivity by ion implanting, then the polycrystalline silicon film is patterned to thereby form a second gate electrode 8 b contacting the first gate electrode 5 a.

Next, as shown in FIG. 6(b), using the second gate electrode 8 b as a mask (the resist used for forming the second gate electrode 8 b may be used as a mask), the sacrifice insulating film 18 is anisotropically etched away to thereby cause the surfaces of the upheaved layers 11 a, 11 b to be exposed.

Next, as shown in FIG. 6(c), a silicon oxide film, for example, is deposited to have about a film thickness of 50 nm and is anisotropically etched, to thereby form sidewall insulating films 19 on the sidewall regions of the gate electrodes 5 a and 8 a.

Next, cobalt, for example, is deposited on the whole surface with a film thickness of about 30 nm to 100 nm by spattering, to thereby form cobalt silicide layers 13 a, 13 b and 13 c. Then, the extra cobalt is etched away, so that the cobalt silicide layers 13 a, 13 b and 13 c are selectively remained.

Next, as shown in FIG. 6(d), an interlayer insulating film 14 and a metal electrode 16 are formed by a method same as that described in the first embodiment, then the manufacturing step of the semiconductor device according to the present embodiment is completed.

FIG. 7 is a plan view showing a third embodiment. FIG. 6(d) is a sectional view taken along the line VII-VII in FIG. 7.

As shown in FIG. 7, in the present embodiment, it is possible to form the silicide layers 13 b, 13 a to extend onto the element-isolation insulating films 7 when the silicide layer 13 c is formed on the gate electrodes 5 a, 8 a, whereby contact openings for connecting the gate electrodes 5 a, 8 a and the metal electrode 16 can be formed on the element-isolation insulating films 7. As such, the element can be miniaturized and the resistance can be reduced.

Forth Embodiment

FIGS. 8(a) through 8(e) and FIGS. 9(a) through 9(d) are schematic sectional views showing a manufacturing method of a semiconductor device according to a forth embodiment of the present invention in the order of steps. In FIGS. 8 and 9, the dimensions in the vertical direction (up and down direction in Figs.) are shown to be enlarged.

The steps of the present embodiment shown up to FIG. 8(d) are same as that of the third embodiment shown in FIGS. 5(a) through 5(d), therefore the explanations are omitted. As shown in FIG. 8(d), explanations will be given for the manufacturing method after it is processed.

As shown in FIG. 8(e), an Al film (20) is deposited on the whole surface by spattering and is etched back (or performed chemical-mechanical polishing) so as to be selectively remained on the upheaved layers 11 a, 11 b to thereby form a sacrifice Al film 20.

Next, as shown in FIG. 9(a), the silicon nitride film 6 on the gate electrode 5 a is selectively etched away using phosphoric acid or the like, and a polycrystalline silicon film is deposited by the CVD, which is given a conductivity by ion implanting and then pattered to thereby form a second gate electrode 8 b contacting the gate electrode 5 a.

Next, as shown in FIG. 9(b), the sacrifice Al film 20 is etched away to thereby cause the surfaces of the upheaved layers 11 a, 11 b to be exposed.

Then, as shown in FIG. 9(c), a silicon oxide film, for example, is deposited to have a film thickness of about 80 nm and is anisotropically etched, whereby sidewall insulating films 19 are formed on the sidewall regions of the gate electrodes 5 a and 8 a.

Then, cobalt, for example, is deposited by spattering on the whole surface to have a film thickness of 30 nm to 100 nm and is performed a heat treatment, to thereby form cobalt silicide layers 13 a, 13 b and 13 c. Then, the extra cobalt is etched away, so that the cobalt silicide layers 13 a, 13 b and 13 c are selectively remained.

Next, as shown in FIG. 9(d), an interlayer insulating film 14 and a metal electrode 16 are formed by a method same as that described in the first embodiment, then the manufacturing step of the semiconductor device according to the present embodiment is completed.

Fifth Embodiment

FIGS. 10(a) to 10(f) and FIGS. 11(a) to 11(f) are schematic sectional views showing a manufacturing method in the order of steps of a semiconductor device according to a fifth embodiment of the present invention. In FIGS. 10 and 11, the dimensions in the vertical direction (up and down direction in Figs.) are shown to be enlarged.

First, as shown in FIG. 10(a), on an SOI substrate which is so formed that a semiconductor layer (silicon layer) 3 having a film thickness of 5 nm to 60 nm is formed on a supporting substrate 1 via a buried insulating film 2, a silicon oxide film 21 is deposited to have a film thickness of about 150 nm.

Next, as shown in FIG. 10(b), the silicon oxide film 21 and the semiconductor layer 3 are selectively etched, whereby the silicon oxide film 21 and the semiconductor layer 3 in the element region are processed to be island shaped.

Then, as shown in FIG. 10(c), a silicon nitride film 7 a is deposited by the CVD so as to be thicker than the total film thickness of the silicon oxide film 21 and the semiconductor layer 3.

Then, as shown in FIG. 10(d), after a predetermined amount of the silicon nitride film 7 a is polished by chemical-mechanical polishing, the silicon nitride film 7 a is etched by plasma etching until the silicon nitride film 21 is exposed on the surface, to thereby form element-isolation insulating films 7 b, the top edge portions of which are flattened. For these element-isolation insulating films 7 b, the silicon nitride film 7 a is used.

Then, as shown in FIG. 10(e), the silicon oxide film 21 is etched away using fluorinated acid to thereby cause the surface of the semiconductor layer 3 to be exposed. In this step, a dented portion for forming upheaved layers 11 a, 11 b described later is formed by the element-isolation insulating films 7 b and the semiconductor layer 3.

Next, as shown in FIG. 10(f), a gate insulating film 4 contacting the surface of the semiconductor layer 3 is formed in the dented portion by a thermal oxidation, then, a first gate material layer 5 consisting of polycrystalline silicon is buried in the dented portion surrounding the semiconductor layer 3 by performing the CVD and chemical-mechanical polishing.

Next, as shown in FIG. 11(a), a second gate material layer 8 consisting of polycrystalline silicon is deposited using the CVD to have a film thickness of about 80 nm, then a mask insulating film 9 a consisting of a silicon oxide film is formed thereon using the CVD as well.

Then, as shown in FIG. 11(b), the mask insulating film 9 a, the second gate material layer 8, and the first gate material layer 5 are patterned to thereby form a first gate electrode 5 a and a second gate electrode 8 a.

Next, as shown in FIG. 11(c), an oxide film is deposited to have, for example, a film thickness of 150 nm using the CVD and is anisotropically etched, to thereby form sidewall insulating films 10 on the sidewalls of the gate electrodes 5 a, 8 a including the mask insulating film 9 a and on the inner sidewalls of the element-isolation insulating films 7 b, respectively.

Next, as shown in FIG. 11(d), a polycrystalline silicon film is deposited to have a film thickness of about 300 nm using the CVD and is flattened by the chemical-mechanical polishing, then the polycrystalline silicon film is etched back, whereby upheaved layers 11 a and 11 b consisting of the polycrystalline silicon film are formed in the dented portions surrounded by the element-isolation insulating films 7 b and the gate electrodes.

Next, impurity atoms of a conductive type opposite to that of the channel are implanted into the second gate electrode 8 a, the first gate electrode 5 a and the upheaved layers 11 a, 11 b by ion implanting and are performed a heat treatment at, for example, 1000° C. for 10 seconds. Thereby, the gate electrodes 5 a, 8 a and the upheaved layers 11 a, 11 b are given conductivities while source/drain regions 3 a and 3 b of a conductive type opposite to that of the semiconductor layer 3 are formed.

Next, as shown in FIG. 11(e), after the mask insulating film 9 a is removed (the mask insulating film 9 a may be removed prior to the ion implanting step), cobalt, for example, is deposited on the whole surface by spattering to have a film thickness of 30 nm to 100 nm and is performed a heat treatment, to thereby form cobalt silicide layers 13 a, 13 b and 13 c. Then, the extra cobalt is etched away, so that the cobalt silicide layers 13 a, 13 b and 13 c are selectively remained. Here, the top surfaces of the upheaved layers 11 a, 11 b and the top surface of the gate electrodes 5 a, 8 a have a difference in their heights. Therefore, a short circuit between them can be prevented.

Then, as shown in FIG. 11(f), an interlayer insulating film 14 consisting of, for example, an oxide film is deposited by the CVD, and the surface of which is flattened by the CMP if necessary, then the interlayer insulating film 14 is selectively etched away to thereby form contact openings 15 a and 15 b. Then, through deposition of a metal film and patterning by the photolithography, a metal electrode 16 contacting the silicide layer via the contact openings is formed, and the manufacturing step of the semiconductor device according to the present embodiment is completed.

Although the present invention has been described above based on the preferred embodiments, the present invention is not limited to these embodiments. The present invention can be modified at any time within a range of not deviating the subject of the present invention. For example, in the first and the third through the fifth embodiments, although the silicide layers are used for both of the upheaved layers and the gate electrodes, either one or the both of them may be made solely of polycrystalline silicon. Further, although the silicide film is formed so as to reduce the resistance of the polycrystalline silicon film, a decrease in the resistance may be achieved by forming a metal film on the polycrystalline silicon film, instead of the silicide film. Moreover, although the upheaved layers are buried in the dented portions by performing both chemical-mechanical polishing and etching in the embodiments, it may be done only by etching.

Industrial Applicability

As described above, in the present invention, element-isolation insulating films are formed to be thicker than a semiconductor layer which is an SOI layer, and a gate electrode is formed to be thicker than the element-isolation insulating films, and upheaved layers are formed in dented portions formed by the gate electrode and the element-isolation insulating films. Thereby, upheaved layers which are thick and low resistance can be formed on source/drain regions without using a lithography process.

Further, in the present invention, the surface height of the gate electrode is set to be higher than the surface height of the upheaved layers, whereby a short circuit between them can be effectively prevented even if a metal silicide film is formed on the upheaved layers and on the gate electrode. 

1. A semiconductor device comprising: a semiconductor layer which is formed on an insulating film or on an insulating substrate while being surrounded by an element-isolation insulating film, and includes a channel region and a source/drain region; a gate electrode which is formed on the channel region via a gate insulating film while being surrounded by a sidewall insulating film; and an upheaved layer which is made of a conductive material and is formed on the source/drain region while being surrounded by the element-isolation insulating film and the gate electrode; wherein the upheaved layer is so formed as to be buried in a dented portion defined by the gate electrode on which the sidewall insulating film is formed and by the element-isolation insulating film on which the sidewall insulating film is formed, while having a height different from that of the gate electrode.
 2. The semiconductor device, as claimed in claim 1, wherein a surface height of the gate electrode is higher than a surface height of the element-isolation insulating film, and a surface height of the upheaved layer is equal to or lower than the surface height of the element-isolation insulating film.
 3. The semiconductor device, as claimed in claim 1, wherein the upheaved layer comprises: a polycrystalline silicon film, or a polycrystalline silicon film and a metal silicide film formed thereon, or a polycrystalline silicon film and a metal film formed thereon, or a metal silicide film, or a metal film.
 4. The semiconductor device, as claimed in claim 1, wherein a film thickness of the semiconductor layer is 30 nm or less.
 5. The semiconductor device, as claimed in claim 1, wherein the gate electrode comprises: a two-layer polycrystalline silicon film, or a two-layer polycrystalline silicon film and a metal silicide film formed thereon, or a two-layer polycrystalline silicon film and a metal film formed thereon.
 6. The semiconductor device, as claimed in claim 1, wherein a film thickness of the upheaved layer is 30 nm or less.
 7. A method of manufacturing a semiconductor device comprising the steps of: (1) forming, on an insulating film or on an insulating substrate, an element-isolation insulating film which surrounds a semiconductor layer serving as a channel region and a source/drain region and has a film thickness thicker than that of the semiconductor layer; (2) forming, on the semiconductor layer via a gate insulating film, a gate electrode, a surface height of which is higher than that of the element-isolation insulating film; and (3) selectively forming, on the semiconductor layer located in a dented portion surrounded by the element-isolation insulating film and the gate electrode, a conductive upheaved layer, a surface height of which is equal to or lower than the surface height of the element-isolation insulating film is added wherein following the step (2) but prior to the step (3), a step of forming sidewall insulating films on a side surface of the gate electrode and on a side surface of the element-isolation insulating film is added.
 8. The method of manufacturing the semiconductor device, as claimed in claim 7, wherein the step (3) includes: a step of depositing a conductive film; and a step of removing an unnecessary conductive film by etching or by chemical-mechanical polishing (CMP) and etching.
 9. The method of manufacturing the semiconductor device, as claimed in claim 7, wherein the upheaved layer is made of polycrystalline silicon, and following the step (3), a step of forming a metal silicide film on the upheaved layer is added.
 10. The method of manufacturing the semiconductor device, as claimed in claim 9, wherein the gate electrode is made of polycrystalline silicon, and in the step (2), a mask insulating film is formed on the gate electrode from which the mask insulating film is removed after the step (3), and in the step of forming the metal silicide film on the upheaved layer, a metal silicide film is also formed on the gate electrode at a same time.
 11. The method of manufacturing the semiconductor device, as claimed in claim 7, wherein a step combining the step (1) and the step (2) includes the steps of: (a) depositing, on the semiconductor layer via the gate insulating film, a first gate forming material layer and a first insulating film which serves as a mask insulating film; (b) patterning the first insulating film, the first gate forming material layer and the semiconductor layer so as to be island shaped; (c) after depositing on a whole surface a second insulating film which serves as the element-isolation insulating film, performing chemical-mechanical polishing so as to remove at least a portion of the first insulating film, to thereby form the element-isolation insulating film surrounding the island-shaped semiconductor layer; and (d) after removing the first insulating film if it exists, depositing a second gate forming material layer and a third insulating film which serves as a mask insulating film, patterning the third insulating film, the second gate forming material layer and the first gate forming material layer, to thereby form the gate electrode having the mask insulating film on a surface thereof.
 12. The method of manufacturing the semiconductor device comprising the steps of: (1) depositing a first gate forming material layer and a mask material layer via a gate insulating film on a semiconductor layer formed on an insulating film or on an insulating substrate; (2) patterning the mask material layer, the first gate forming material layer and the semiconductor layer so as to be island shaped, and filling an element-isolation groove formed with an element-isolation insulating film; (3) patterning the mask material layer and the first gate forming material layer to thereby form a first gate electrode; (4) forming first sidewall insulating films on a side surface of the element-isolation insulating film and on a side surface of a laminated body formed of the mask material layer and the first gate electrode; (5) filling a dented portion surrounded by the first sidewall insulating films on the semiconductor layer with a conductive upheaved layer and a sacrifice filler; and (6) after removing the mask material layer, depositing a second gate forming material layer and patterning it, to thereby form a second gate electrode.
 13. The method of manufacturing the semiconductor device, as claimed in claim 12, further comprising, following the step (6), a step of removing at least the sacrifice filler on the upheaved layer, forming a second sidewall insulating film on a side surface of the second gate electrode, and forming a metal silicide layer on top surfaces of the upheaved layer and the second gate electrode is added.
 14. The method of manufacturing the semiconductor device, as claimed in claim 12, wherein the mask material layer is a silicon nitride film, and the sacrifice filler is a silicon oxide film or a metal film.
 15. The method of manufacturing the semiconductor device, as claimed in claim 12, wherein the step (5) includes the steps of: (a) depositing a conductive material on a whole surface, and forming, by etching or by chemical-mechanical polishing and etching, the upheaved layer so that the conductive material is remained to have a film thickness which is less than a depth of the dented portion; and (b) depositing a material serving as the sacrifice filler, and filling the dented portion with the sacrifice filler by performing chemical-mechanical polishing.
 16. (canceled) 